LQ-Self-flow Castable
Corundum Based Self-flow Castable
Al2O3+MgO		Bulk density	C.C.S		Modulus of rupture		Water addition
		110ºC*16h 1500ºC*3h	110ºC*16h	1500ºC*3h	110ºC*16h	1500ºC*3h
(% minm)		(gm./cc minm)	(MPa minm)		(MPa minm)		(%)
85		2.85	30	85	4	12	5.0＼0.5
90		2.85	30	85	4	12	5.0＼0.5
Applications: Ladle bottom, around seating block, gap filling
HIgh alumina Based Self-flow Castable
Al2O3	Bulk density		C.C.S		Modulus of rupture		Water addition
	110ºC*16h	1350ºC*3h	110ºC*16h	1350ºC*3h	110ºC*16h	1350ºC*3h
(% minm)	(gm./cc minm)		(MPa minm)		(MPa minm)		(%)
50	2.2	2.15	30	50	4	12	7-9
60	2.3	2.25	30	60	4	12	7-9
Applications: Permanent lining of ladle and tundish