Properties for LQ/VSV-C51 slide plate

Chemical and Physical Properties	LQ-Series Ladle Slide Gate Plate £¨General£©
	Magnesia material	Al-C	Al- Zr-C
apparent porosity  %  max	10	8	8
Bulk Density   g/cm3  min	3.0	3.05	3.1
Compressive strength   MPa   min	120	120	120
Al2O3  %   min	8	85	85
ZrO2   %   min			4
C    %    min	3	3	3
MgO   %	65 min
Service Life  heats	1-2	1-3	1-5

Sample order (10 pcs at least) will be produced for testing.